Flux cored solder wire with powerful wetting

S3X-72M
Sn 3.0Ag 0.5Cu

Designed for Faster Soldering and Improved Wettability

Prevents bridging in slide soldering

72M series contain new activators for improved wettability and new resin composition for better flux coverage. They can prevent bridging even at defect prone conditions such as low iron tip temperature or fast sliding speed.

High in electrical reliability

With the activation level of flux being categorized as ROL0, 72M series prevent electro-migration and secure high surface insulation resistance. For better usability, they emit less amount of fume when soldering and leave clearer flux residue.

Superior wetting properties

New activators with superior activation characteristics successfully remove oxide film from the surfaces to be soldered. As a result, S3X-72M exhibits high wettability not only to Cu, but also to “difficult to wet” merals such as Ni and Brass

Product Performance Table

Product Name
S3X-72M
Product Category
Flux Cored Solder Wire
Melting Point(℃)
217-219
Flux Content(%)
3.2
Halide content(%)
< 0.01
Flux Type
ROL0 (IPC J-STD-004)
Diameter(mm φ)
0.3, 0.5, 0.6, 0.8, 1.0 ,1.2